Home> Products> Polyurethane System For Shoe Sole> Polyurethane System For Lady's Shoe Sole Raw Material Polyester Resin Pu Hard Materials> PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness
PU for lady's shoe light weight high hardness

PU for lady's shoe light weight high hardness

Get Latest Price
Payment Type:L/C,T/T,D/P
Incoterm:FOB,CFR,CIF
Min. Order:1000 Kilogram
Transportation:Ocean
Port:Shanghai
Product Attributes

Model No.XC-9080W/XC-6088W

BrandXuchuan

Place Of OriginChina

Types OfSynthetic Resin And Plastics

ChemicalPU

Keywordsflexible polyurethane resin

CharacteristicLow density and high hardness, good appearance, little pinhole, and weak foam line

ApplicationOutsole, slippers, wedge shoes

CodeXC-9080W/XC-6088W

BrandXUCHUAN

Packaging & Delivery
Selling Units : Kilogram
Package Type : 20 & 225 kg/drum
Picture Example :
Product Description

PRODUCT DESCRIPTION

Women'S Shoe Sole

Polyol and Isocyanate flexible polyurethane resin casting for shoe sole

Low density and high hardness, good appearance, little pinhole, and weak foam line


Raw Material Polyester Resin

Product Detail

Application shoe sole
Keywords flexible polyurethane resin
A/B Materials Temperatures(℃) A/B Materials Temperatures(℃)
A+C/B Mix ratio (By weight) 100/100~102
Cream Time (s) 6~8
End of Rise Time (s) 30~40
Free Rise Foam Density(g/cm3) 0.21~0.26
Mold Temperature(℃) 45~55
Demold Time(min) Demold Time(min)
Molded Density (g/cm3) 0.35~0.60

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line

Application: Outsole, slippers, wedge shoes

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

/

/

A-9080W

Cream,White,liquid

1000~1300

1.01~1.02

18

/

/

/

B-6088

Yellowish transparent liquid or waxy

600~800

1.08~1.2

20

/

/

/

Materials preheat

A-9080W:  preheated at 50~60 for 6~8 hours.

B-6088:    preheated at 50~60 for 6~8 hours.

Typical processing parameters & Reaction parameter.

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/100~102

6~8

30~40

0.21~0.26

45~55

5~7

The adding content of C-2 should be 210g±10g/18kg.

The adding content of water should be 0~80g/18kg according to the reality.

The adding content of hardener should be 0~1200g/18kg according to the reality.

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
(%)

Tear Strength
(kN/m)

Williams abrasion
(cc/php)

/

Physical  properties

0.35~0.60

60~88

4~7

200~300

11~20

130~200

/

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Pu Hard Materials


COMPANY PROFILE

PRODUCTION PROCESS
CERTIFICATION
PACKAGING AND SHIPPING
FAQ

CONTACT US
Send Inquiry
*
*

We will contact you immediately

Fill in more information so that we can get in touch with you faster

Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.

Send