polyurethane resin material for casting straps sandals
polyurethane resin material for casting straps sandals
polyurethane resin material for casting straps sandals
polyurethane resin material for casting straps sandals
polyurethane resin material for casting straps sandals
polyurethane resin material for casting straps sandals

polyurethane resin material for casting straps sandals

Payment Type: L/C,T/T
Incoterm: FOB,CIF
Min. Order: 17600 Kilogram
Delivery Time: 15 Days

Contact Now Add to Basket

Basic Info

    Model No.: A-9088W,B-6088

Additional Info

    Packaging: 220kg/drum

    Productivity: 260000tons/month

    Brand: Xuchuan Chemical

    Transportation: Ocean,Land

    Place of Origin: China

    Port: Shanghai

Product Description

PRODUCT DESCRIPTION

Pu molding Polyurethane Resin material for casting straps sandals

Product Detail

Application shoe sole
Keywords pu molding,polyurethane resin for casting,material straps for sandals
A/B Materials Temperatures(℃) A/B Materials Temperatures(℃)
A+C/B Mix ratio (By weight) 100/100~102
Cream Time (s) 6~8
End of Rise Time (s) 30~40
Free Rise Foam Density(g/cm3) 0.21~0.26
Mold Temperature(℃) 45~55
Demold Time(min) Demold Time(min)
Molded Density (g/cm3) 0.35~0.60

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line

Application: Outsole, slippers, wedge shoes

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

/

/

A-9080W

Cream,White,liquid

1000~1300

1.01~1.02

18

/

/

/

B-6088

Yellowish transparent liquid or waxy

600~800

1.08~1.2

20

/

/

/

Materials preheat

A-9080W: preheated at 50~60 for 6~8 hours.

B-6088: preheated at 50~60 for 6~8 hours.

Typical processing parameters & Reaction parameter.

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/100~102

6~8

30~40

0.21~0.26

45~55

5~7

The adding content of C-2 should be 210g±10g/18kg.

The adding content of water should be 0~80g/18kg according to the reality.

The adding content of hardener should be 0~1200g/18kg according to the reality.

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
(%)

Tear Strength
(kN/m)

Williams abrasion
(cc/php)

/

Physical properties

0.35~0.60

60~88

4~7

200~300

11~20

130~200

/

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


COMPANY PROFILE

PRODUCTION PROCESS
CERTIFICATION
PACKAGING AND SHIPPING
FAQ

CONTACT US

Looking for ideal Pu Molding for Shoes Manufacturer & supplier ? We have a wide selection at great prices to help you get creative. All the Polyurethane Resin for Casting are quality guaranteed. We are China Origin Factory of Material Straps for Sandals. If you have any question, please feel free to contact us.

Product Categories : Polyurethane System For Shoe Sole > Polyurethane System For Sandals and Slippers

Email to this supplier

Your message must be between 20-8000 characters

Related Products List