Home> Products> Casting Polyurethane Prepolymer> CPU For Rubber Roller Castor Wheel> Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base
Polyester and Polyether Prepolymer in PTMEG PPG Base

Polyester and Polyether Prepolymer in PTMEG PPG Base

Get Latest Price
Payment Type:L/C,T/T,D/P
Incoterm:FOB,CFR,CIF
Min. Order:1000 Kilogram
Transportation:Ocean
Port:Shanghai
Product Attributes

Model No.XCPU-E136

BrandXUCHUAN

Place Of OriginChina

Types OfSynthetic Resin And Plastics

ApplicationRoller

Appearancessolid

UsesSieve, machinery parts, sealing ring, PU roller and other products

Featuresexcellent wear resistance, oil resistance, mechanical properties

CodeXCPU-E136

BrandXUCHUAN

Package(kg)20 / 200

Packaging & Delivery
Selling Units : Kilogram
Package Type : 20 & 200 KG/DRUM
Picture Example :
Product Description


PRODUCT DESCRIPTION

Cpu For Tyres Wheel

Polyester and Polyether Prepolymer in PTMEG and PPG Base

Custom Prepolymer For Wheel

Product Detail

Viscosity(mPa.s/85 ℃) 1800-2000
NCO% content 3.60-3.80
Package(kg) 20 / 200
MOCA Level(%) 10.8
Recommended % Theory(%) 95
Prepolymer Temperature(℃) 75-85
Curative Temperature(℃) 110-120
Pot Life(mins) 10
Demould Time(@ 100°C (hrs)) 1
Post Cure Time(@ 100°C (hrs)) 10

1、This product is a Polyester Polyol and toluene diisocyanate (T-100) in the synthesis of polyester polyurethane prepolymer.

2、Features: excellent wear resistance, oil resistance, mechanical properties.

3、Uses:Sieve, machinery parts, sealing ring, PU roller and other products.

4、Product Specifcation:

Name of products

Appearances

Viscosity(mPa.s/85 )

NCO% content

Package(kg)

XCPU-E136

solid

1800-2000

3.60-3.80

20 / 200

5、Mixing and Curing Conditions:

MOCA Level

Recommended
% Theory

Prepolymer
Temperature

Curative Temperature

Pot Life

Demould Time

Post Cure Time

%

%

mins

@ 100°C(hrs)

@ 100°C(hrs)

10.8

95

75-85

110-120

10

1

10

6、Processing Procedure:

Prepolymer at 75 ~ 85 ℃ preheating, after vacuum degassing, the

melt MOCA good homogeneous mixing, deaeration, pouring, molding,

vulcanization molding, stripping, vulcanization.

7、Physical Properties:

Properties presented below are to be used as a guide and not intended

for specification purposes.

Hardness

Tensile Strength

100% Modulus

300% Modulus

Angle Tear Strength,
Die C

Trouser Tear Strength

Elongation

Resilience

DIN Abrasion
Resistance 10N

Cured Specific
Gravity

Shore A

MPa

MPa

MPa

kN/m

kN/m

%

%

mm3

g/cm3

85

48

4.2

3.8

75

34

670

39

40

1.26

Precautions:

1, The product is easy to absorb moisture, will lead to product deterioration in the transportation, storage and use shall be kept sealed packaging good, original sealed storage for six months after opening, to be used up as quickly as possible to prevent moisture absorption metamorphism; If you can not run out of time, to be purged with nitrogen and sealed.

2, The information listed in this specification, may be due to product renewal and change, in view of processing technology, formulation and processing and other applications Not the same, pre-test their applicability in case of application of the product, please contact the

XUCHUAN chemical research and development or technical service department.

Pu Casting Gear Wheel


COMPANY PROFILE

PRODUCTION PROCESS
CERTIFICATION
PACKAGING AND SHIPPING
FAQ


Home> Products> Casting Polyurethane Prepolymer> CPU For Rubber Roller Castor Wheel> Polyester and Polyether Prepolymer in PTMEG PPG Base
Send Inquiry
*
*

We will contact you immediately

Fill in more information so that we can get in touch with you faster

Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.

Send