PU resin for making slipper and sandal
Get Latest PricePayment Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. Order: | 1000 Kilogram |
Transportation: | Ocean |
Port: | Shanghai |
Payment Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. Order: | 1000 Kilogram |
Transportation: | Ocean |
Port: | Shanghai |
Model No.: XC-2260/XC-8580
Brand: Xuchuan Chemical
Application: Shoes
Place Of Origin: China
Types Of: Synthetic Resin And Plastics
Code: XC-2260/XC-8580
Characteristic: Good handle, low density and good dimension stability
Appearance: liquid
PU resin for making slipper and sandal
Application | shoe sole |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 40~50 |
Free Rise Foam Density(g/cm3) | 0.15~0.25 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 2.5~3.5 |
Molded Density (g/cm3) | 0.30~0.45 |
Hardness(Shore A ) | 43~58 |
Tensile strength(MPa) | 1.5~4.5 |
Elongation(%) | 250~400 |
Polyurethane for footwear sole:
Density:300~500 kg/m3.
Hardness:45~75shore A.
Good compatibility with pigments.
Widely ratio.
Characteristic: Good handle, low density and good dimension stability | |||||||
Application: Outsole and mid-sole | |||||||
Typical properties of PU matrix | |||||||
Name of products | Appearance | Viscosity (mPa·s/40℃) | Density (g·cm-3/40℃) | Package(kg) | / | / | / |
A-2260 |
Cream white liquid | 800~1200 | 1.01~1.02 | 18 | / | / | / |
B-8580 |
Yellowish transparent liquid or waxy | 600~800 | 1.08~1.2 | 20 | / | / | / |
Materials preheat | |||||||
A-2260: preheated at 50~60℃ for 8~10 hours | |||||||
B-8580: preheated at 50~60℃ for 8~12 hours | |||||||
Typical processing parameters & Reaction parameter | |||||||
Items | A/B Materials Temperatures(℃) | A+C/B Mix ratio (By weight) | Cream Time (s) | End of Rise Time (s) | Free Rise Foam Density(g/cm3) | Mold Temperature(℃) | Demold Time(min) |
Parameter | 40~45/38~42 | 100/96~98 | 6~8 | 40~50 | 0.15~0.25 | 45~55 | 2.5~3.5 |
The adding content of C-2 should be 270g±20g/18kg | |||||||
The adding content of water should be 0~100g/18kg according to the reality | |||||||
The adding content of hardener should be changed according to the reality | |||||||
Physical properties | |||||||
Items | Molded Density (g/cm3) | Hardness (Shore A ) | Tensile strength (MPa) | Elongation (%) | Tear Strength (kN/m) | Ross Flexing (room temperature) ( 40,000 times) | / |
/ | |||||||
/ | |||||||
Physical properties | 0.30~0.45 | 43~58 | 1.5~4.5 | 250~400 | 10~26 | No crack | / |
Demold time may be prolonged with the increase of sole thickness | |||||||
These physical data are acquired by testing a sample of 6mm thick. | |||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.