Polyurethane for making slipper and sandal
Polyurethane for making slipper and sandal
Polyurethane for making slipper and sandal
Polyurethane for making slipper and sandal
Polyurethane for making slipper and sandal
Polyurethane for making slipper and sandal

Polyurethane for making slipper and sandal

Get Latest Price
Incoterm:FOB,CFR,CIF
Min. Order:1000 Kilogram
Transportation:Ocean
Port:Shanghai
Product Attributes

Model No.A-2260/B-8580

BrandXuchuan Chemical

Place Of OriginChina

Types OfSynthetic Resin And Plastics

ApplicationOutsole and mid-sole

CharacteristicGood handle, low density and good dimension stability

AppearanceLiquid

Packaging & Delivery
Selling Units : Kilogram
Package Type : 20&225kg/drum
Picture Example :
Product Description

PRODUCT DESCRIPTION

Polyurethane Raw Materials

Pu resin two component polyurethane sealant transparent thermoplastic for making slipper and sandal

Shoe Sole Pu Chemical


most popular grade

Raw Material Polyester Resin

Product Detail

Application shoe sole
Cream Time (s) 6~8
End of Rise Time (s) 40~50
Free Rise Foam Density(g/cm3) 0.15~0.25
Mold Temperature(℃) 45~55
Demold Time(min) 2.5~3.5
Molded Density (g/cm3) 0.30~0.45
Hardness(Shore A ) 43~58
Tensile strength(MPa) 1.5~4.5
Elongation(%) 250~400

Polyurethane for footwear sole: 

  • Density:300~500 kg/m3.

  • Hardness:45~75shore A.

  • Good compatibility with pigments.

  • Widely ratio.

Characteristic: Good handle, low density and good dimension stability

Application: Outsole and mid-sole

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

/

/

A-2260

Cream white liquid

800~1200

1.01~1.02

18

/

/

/

B-8580

Yellowish 

transparent 

liquid or waxy 

600~800

1.08~1.2

20

/

/

/

Materials preheat

A-2260:  preheated at 50~60 for 8~10 hours          

B-8580:  preheated at 50~60 for 8~12 hours

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures()

A+C/B Mix ratio

(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/96~98

6~8

40~50

0.15~0.25

45~55

2.5~3.5

The adding content of C-2 should be 270g±20g/18kg

The adding content of water should be 0~100g/18kg according to the reality

The adding content of hardener should be changed according to the reality

Physical properties

Items

Molded Density (g/cm3)

Hardness

(Shore A )

Tensile strength

(MPa)

Elongation

(%)

Tear Strength

(kN/m)

Ross Flexing

(room temperature)

( 40,000 times)

/

/

/

Physical  properties

0.30~0.45

43~58

1.5~4.5

250~400

10~26

No crack

/

Demold time may be prolonged with the increase of sole thickness

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


Company Overview

company   company

    Xuchuan chemical established in 2007, company registered capital is RMB 500 million. The main products are all ranges polyester polyol, polyurethane resin for shoes, water-based and solvent-free polyurethane resins for artificial leather, polyurethane bonding adhesives and polyurethane hot melt adhesives.

    Now Xuchuan has 4 modern production bases, production capacity reached 630,000 tons per year, products exported to 32 countries and regions in the world.

Workshop
Certificate
Exhibition
R&D Department
Cooperative Customers
Packing and shipping


FAQ
Send Inquiry
*
*

We will contact you immediately

Fill in more information so that we can get in touch with you faster

Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.

Send