Polyol and Isocyanate for Lady's Wedge Shoe Sole
Get Latest PricePayment Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. Order: | 1000 Kilogram |
Transportation: | Ocean |
Port: | Shanghai |
Payment Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. Order: | 1000 Kilogram |
Transportation: | Ocean |
Port: | Shanghai |
Model No.: XC-9080W/XC-6088W
Brand: Xuchuan Chemical
Place Of Origin: China
Application: Outsole, slippers, wedge shoes
Code: XC-9080W/XC-6088W
Keywords: water soluble polyurethane resin
Appearance: Liquid
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Application | shoe sole |
Keywords | water soluble polyurethane resin |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line | |||||||
Application: Outsole, slippers, wedge shoes | |||||||
Typical properties of PU matrix | |||||||
Name of products | Appearance | Viscosity (mPa·s/40℃) | Density (g·cm-3/40℃) | Package(kg) | / | / | / |
A-9080W |
Cream,White,liquid | 1000~1300 | 1.01~1.02 | 18 | / | / | / |
B-6088 | Yellowish transparent liquid or waxy | 600~800 | 1.08~1.2 | 20 | / | / | / |
Materials preheat | |||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. | |||||||
B-6088: preheated at 50~60℃ for 6~8 hours. | |||||||
Typical processing parameters & Reaction parameter. | |||||||
Items | A/B Materials Temperatures(℃) | A+C/B Mix ratio | Cream Time (s) | End of Rise Time (s) | Free Rise Foam Density(g/cm3) | Mold Temperature(℃) | Demold Time(min) |
Parameter | 40~45/38~42 | 100/100~102 | 6~8 | 30~40 | 0.21~0.26 | 45~55 | 5~7 |
The adding content of C-2 should be 210g±10g/18kg. | |||||||
The adding content of water should be 0~80g/18kg according to the reality. | |||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. | |||||||
Physical propertiesShoe Sole Pu Chemical | |||||||
Items | Molded Density (g/cm3) | Hardness | Tensile strength | Elongation | Tear Strength | Williams abrasion | / |
Physical properties | 0.35~0.60 | 60~88 | 4~7 | 200~300 | 11~20 | 130~200 | / |
Demold time may be prolonged with the increase of sole thickness. | |||||||
| |||||||
|
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.
pu system for shoe sole, adhesive for shoes,cpu,tpu,Polyester Polyol,pu resin for ink,PUR Hot Melt Adhesive,adhesive for flexible package,PU Resin For Synthetic Leather
Xuchuan chemical established in 2007, company registered capital is RMB 500 million. The main products are all ranges polyester polyol, polyurethane resin for shoes, water-based and solvent-free polyurethane resins for artificial leather, polyurethane bonding adhesives and polyurethane hot melt adhesives.
Now Xuchuan has 4 modern production bases, production capacity reached 630,000 tons per year, products exported to 32 countries and regions in the world.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.